Post epitaxial thermal oxidation

ABSTRACT

Disclosed is a system and method for handling post epitaxial thermal oxidation. The method produces semiconductor wafers by performing the steps of forming a wafer substrate, depositing an epilayer on the substrate, oxidizing a top portion of the epilayer, and removing the oxidized top portion. As a result, the wafer&#39;s surface is very smooth, with little or no micro-steps thereon.

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] This application relies on U.S. Provisional Patent Application No. 60/072,046, entitled “Post Expitaxial Thermal Oxidation,” filed Jan. 21, 1998.

TECHNICAL FIELD

[0002] This invention relates generally to semiconductor wafer production.

BACKGROUND OF THE INVENTION

[0003] In general, semiconductor wafers are prepared in several steps, including (1) growing a single crystal ingot out of molten silicon, (2) sawing the single crystal ingot into wafers, (3) shaping or lapping the wafers, (4) performing a rough polish, and (5) depositing an epi layer of silicon substrate. The epi layer is often deposited using chemical vapor, high temperature deposition to form a single crystal silicon layer on the surface of the wafer. Once the wafers have been prepared, they are provided to a fabrication facility (fab) for further processing.

[0004] As fabs are processing smaller and smaller line widths and devices are continually shrinking, the wafer surface effects the entire fab processing. Furthermore, a particle that used to be “invisible” can now completely ruin a device. Also, the surface of an epitaxial wafer exhibits characteristics known as “micro-steps.” Micro-steps occur because the surface of the wafer is crystal and when it is sawed, the surface is dis-oriented with respect to the crystal graphic plains. Therefore, despite the wafers being sawn and polished, the resulting surface has these micro-steps across its surface.

SUMMARY OF THE INVENTION

[0005] In response to the problems discussed above, described herein is a system and method for handling post epitaxial thermal oxidation. In one embodiment, the method produces semiconductor wafers by performing the steps of forming a wafer substrate, depositing an epilayer on the substrate, oxidizing a top portion of the epilayer, and removing the oxidized top portion. As a result, the wafer include's an epi-surface that is very smooth, with little or no micro-steps thereon.

BRIEF DESCRIPTION OF THE DRAWINGS

[0006]FIGS. 1a, 1 b are cross sectional views of a wafer with an epitaxial layer deposited thereon.

[0007]FIG. 2 is a flowchart of a method to be performed on the wafer of FIG. 1.

[0008]FIG. 3 is a cross sectional view of the wafer of FIGS. 1a, 1 b with an oxide layer on a top surface thereof.

[0009]FIG. 4 is a cross sectional view of the wafer of FIG. 2 after the oxide layer has been removed.

DESCRIPTION OF THE PREFERRED EMBODIMENT

[0010] Referring to FIG. 1a, a semiconductor wafer substrate 10 has deposited on its top surface 12 an epitaxial layer 14. Fabricating an epitaxial layer on a wafer is well known in the art and will not be further discussed. However, referring to FIG. 1b, it becomes evident that small micro steps 16 are formed on a top surface 18 of the epilayer 14.

[0011] Referring to FIGS. 2 and 3, a method 50 is used to reduce the size of the micro steps 16 (as well as remove any particles) from the top surface 18 of the epilayer 14. At step 52, an oxidation layer 60 is deposited or grown on the epilayer 14 using thermal oxidation. During this step 52, a portion of the epilayer (silicon) is consumed by the oxygen. As a result, the previous epi-surface 18 no longer exists and a new, smoother epi/oxide interface 62 is formed. At step 54, the oxide layer 60, including the consumed silicon that previously existed between the epi-surface 18 and the epi/oxide interface 62, is removed.

[0012] Referring to FIG. 4, as a result, a resultant epi-surface 64 is formed on the epilayer 14. The epi-surface 64 is relatively smooth, as compared with the epi-surface 18. 

What is claimed is:
 1. A method for producing semiconductor wafers: forming a wafer substrate; depositing an epilayer on the substrate; oxidizing a top portion of the epilayer; and removing the oxidized top portion. 